PU sheet and polyurethane sheet :

Description: the polyurethane elastomeric is a new material of polymer synthetic between rubber and plastic. It has both high strength of plastic and high elasticity of rubber. Its characteristics are: 1, a wide range of hardness. It still has rubber elongation and resilience at high hardness. The polyurethane elastomeric has a hardness range of Shore A10-D80. 2. high strength. At rubber hardness, the tensile strength, tear strength and load carrying capacity are much higher than general rubber material. At high hardness, its impact strength and flexural strength are much higher than plastic material. 3, wear-resistant. Its wear resistance is very outstanding, generally in the range of 0.01-0.10cm3/1.61km, about 3-5 times than rubber material. 4, oil resistant. The polyurethane elastomeric is a highly polar polymer compound which has low affinity with non-polar mineral oil and is hardly eroded in fuel oil and mechanical oil. 5, good resistance to oxygen and ozone. 6, excellent vibration absorption performance, can do damping and buffering. In the mold manufacturing industry, it replaces rubber and springs.7, has good low temperature performance. 8, radiation resistance. Polyurethane is highly resistant to high energy radiation and has satisfactory performance at 10-10 deg radiation dose. 9, with good machining performance.

The polyurethane sheet, pu sheet are made by mould cast or centrifuge rotor with high quality polyester or polyether material. It is very good performance of chemic erode resistant, impregnant resistant, ozone resistant, radiation resistant, aging resistant, hydrolyze resistant, and high tensile strength, tear resistant, high impact resistant, high bend strength and low compression set etc. The abrasion resistant is 5 multiple more than pure natural rubber, and the oil resistant is 3-5 multiple more than NBR rubber, and have high elasticity 65% with prominent compression resistant at high temperature. wider revise hardness range of 75-95shore A, very good viscidity with metal material, it is a new macromolecule material with fast evolutive now. Apply to military, mine, oil field, chemical, printing, punch, paper making, shoe making, spin, auto industrial etc.

Specifications:

material: virgin CPU of polyether or polyester

color: clear yellow, transparent, black, red, brown, white, blue, green etc.

surface: smooth/smooth

tensile strength: 25-50Mpa

elasticity impact: >25%

hardness: 75-95shore A

elongation: 400%-600%

density: 1.15-1.25g/cm3

tear strength: 35-155KN/m

akron abrasion loss:<0.05cm3/1.61km

compression set (22h*70°C):<10%

working temperature: 120°C(maximum)

thickness: 0.1-60mm

width: 10-1500mm

length: 500-4900mm

standard size: 

0.1-3.0mm x 1.00m x 50kgs

0.1-3.0mm x 1.22m x 50kgs

0.1-3.0mm x 1.37m x 50kgs

1-20mm x 0.3m x 3.0m

1-20mm x 0.6m x 3.0m

1-20mm x 0.4m x 4.0m

1-20mm x 0.5m x 4.0m

1-20mm x 0.6m x 4.0m

1-20mm x 0.8m x 4.0m

1-20mm x 1.0m x 4.0m

1-20mm x 1.2m x 4.0m

1-20mm x 1.5m x 4.9m

10-60mm x 0.3m x 0.3m

10-60mm x 0.4m x 0.4m

10-60mm x 0.5m x 0.5m

10-60mm x 0.6m x 0.6m

10-60mm x 0.5m x 1.0m

10-60mm x 0.6m x 1.2m

10-60mm x 1.0m x 1.0m

10-60mm x 1.0m x 2.0m

OEM & customized size are agreed

packing in cartons, pallets or crates

***when you enquiry, pls confirm the material, color, hardness, size and quantity***

0.1-3.0mm x 1.00m x 50kgs

0.1-3.0mm x 1.22m x 50kgs

0.1-3.0mm x 1.37m x 50kgs

1-20mm x 0.3m x 3.0m

1-20mm x 0.6m x 3.0m

1-20mm x 0.4m x 4.0m

1-20mm x 0.5m x 4.0m

1-20mm x 0.6m x 4.0m

1-20mm x 0.8m x 4.0m

1-20mm x 1.0m x 4.0m

1-20mm x 1.2m x 4.0m

1-20mm x 1.5m x 4.9m

10-60mm x 0.3m x 0.3m

10-60mm x 0.4m x 0.4m

10-60mm x 0.5m x 0.5m

10-60mm x 0.6m x 0.6m

10-60mm x 0.5m x 1.0m

10-60mm x 0.6m x 1.2m

10-60mm x 1.0m x 1.0m

10-60mm x 1.0m x 2.0m

OEM & customized size are agreed

clear yellow, transparent, black, red, brown, white, blue, green etc.

 Apply to military, mine, oil field, chemical, printing, punch, paper making, shoe making, spin, auto industrial etc.

tensile strength: 25-50Mpa

elasticity impact: >25%

hardness: 75-95shore A

elongation: 400%-600%

density: 1.15-1.25g/cm3

tear strength: 35-155KN/m

akron abrasion loss:<0.05cm3/1.61km

compression set (22h*70°C):<10%

working temperature: 120°C(maximum)